Steel with considerable Chromium content that with the addition of Phosphorus and Sulfur, make it a free machining steel, is the most machinable of all stainless steels. A very wide range of mechanical properties can be obtained with a conventional heat treatment, it is magnetic in all its states, manufactured by electric furnace, it is a high quality steel, free of any defect and widely used in the aeronautical and food industry.

Stainless Steel AISI 416 APPLICATIONS

Screws
Nuts
Small turned and milled metal parts
Complex shape axes

Description	Value - Unit	Specification
Tensile strength kg/cm2	5275	Annealed (760ºC) 1"Ø
Cedence point	2815	Annealed (760ºC) 1"Ø
Elongation 5.08 cm	35	Annealed (760ºC) 1"Ø
Area Reduction	70	Annealed (760ºC) 1"Ø
Brinell hardness	185	Annealed (760ºC) 1"Ø
Tensile strength kg/cm2	9000	Tempering (1010ºC) and Tempering (600ºC) 1"Ø
Cedence point	7700	Tempering (1010ºC) and Tempering (600ºC) 1"Ø
Elongation 5.08 cm	17	Tempering (1010ºC) and Tempering (600ºC) 1"Ø
Area Reduction	70	Tempering (1010ºC) and Tempering (600ºC) 1"Ø
Brinell hardness	285	Tempering (1010ºC) and Tempering (600ºC) 1"Ø
Tensile strength kg/cm2	12000	Tempering (815ºC) and Tempering (540ºC) 1"Ø
Cedence point	9500	Tempering (815ºC) and Tempering (540ºC) 1"Ø
Elongation 5.08 cm	15	Tempering (815ºC) and Tempering (540ºC) 1"Ø
Area Reduction	45	Tempering (815ºC) and Tempering (540ºC) 1"Ø
Brinell hardness	350	Tempering (815ºC) and Tempering (540ºC) 1"Ø