Titanium Alloy Grade 16

Titanium alloys have many good attributes such as superior corrosion resistance, very high tensile strength, and durability.

Grade 16 Ti-0.05Pd alloy is comparatively lower in cost, and a leaner palladium version of grade 7. This alloy is similar to grade 7 with respect to physical/mechanical properties and corrosion resistance. The presence of palladium helps to enhance the alloy's corrosion resistance. Grade 16 has good formability.

 

Professional titanium material supplier - GNEE

 

Common Name
CP Grade 16	CP Grade 16
CP Grade 2 with Lower Palladium	CP Grade 2 with Lower Palladium
Titanium Grade 16
UNS
R52402
General Information
Ti Grade 16 is an unalloyed titanium grade with standard oxygen content and addition of palladium (0.04–0.08%). The material has good toughness and is readily weldable. This material is very corrosion resistant in highly oxidizing and mildly reducing environments. The material is castable and is often utilized in cast valves and fittings. In plate form, the alloy is also used explosively boned to make clad plate. The alloy is available as castings, wire, welded tube, pipe, plate, sheet, strip, forgings, bar, and billet.
Common Specification
Specification	Product Form
ASME SB-265	Sheet, Strip and Plate
ASME SB-338	Seamless and Welded Tube
ASTM B265 (Grade 16)	Sheet, Strip and Plate
ASTM B348 (Grade 16)	Bars and Billets
ASTM B367 (Grade Ti-Pd 16)	Castings
AWS A5.16 ERTi-16	Weld Wire

 

Chemistry Requirements
N	C	>H	Fe	O	Pd	Residual Each Max	Residuals Max Total	Ti
0.03	0.1	0.015	0.30	0.25	0.04-0.08	0.1	0.4	Balance

% Maximum unless given as a range.

 

Minimum Tensile Properties
Condition	UTS ksi (Mpa)	>0.2%YS ksi (MPA)	% El.	% RA*
As specified (shape)	50 (345)	40 (275)	20	30

 

 

Typical Tensile Properties
Condition	UTS ksi (Mpa)	>0.2%YS ksi (MPA)	% El.	% RA*
As provided	70 (438)	51 (352)	28	–

 

Welding
Weldability of grade 16 Ti-0.05Pd alloy is rated as very good. This alloy is a single-phase material, hence the microstructure of the alpha phase is not affected by thermal treatments or welding temperatures.

Annealing
Annealing of this material can be performed by heating to 650-760°C (1202-1400°F) for 6 min to 2 h and then air cooled. In case stress relieving is required, the material has to be heated to 480-595°C (896-1103°F) for 15 min to 4 h, and then air cooled.

 

Large-scale factory production

Q:Does the product have quality inspection before loading?
A:Of course, all our products are strictly tested for quality before packaging, and unqualified products will be destroyed.

Q:How to pack the products?
A:The inner layer has a waterproof paper outer layer with iron packaging and is fixed with a fumigation wooden pallet. It can effectively protect products from corrosion during ocean transportation.

Q:What is your working time?
A:In general, our online service time is time: 9:00-22:00, after 22:00, we will reply to your inquiry during the next working day.
Q: What trade terms do you usually use?
A: We use FOB, CIF, EXW,FCA,FAS,CFR.

Hot Tags: Titanium Alloy Grade 16,Titanium