Product Details
This datasheet applies to 430 / 1.4016 general purpose stainless steel hot and cold rolled sheet / strip, semi-finished products, bars, wires, profiles and glossy products.
App
Railway and road vehicles, container construction, sugar storage and transportation, sound absorbers, coal mines This steel is resistant to intergranular corrosion.
Chemical composition
Element | % existing (in product form) | |
C, H, P | L | |
Carbon (C) | ≤0.08 | ≤0.08 |
Silicon (Si) | ≤1.00 | ≤1.00 |
Manganese (Mn) | ≤1.00 | ≤1.00 |
Phosphorus (P) | ≤0.040 | ≤0.040 |
Sulfur (S) | ≤0.015 | ≤0.0301) |
Chromium (Cr) | 16.00 - 18.00 | 16.00 - 18.00 |
Iron (Fe) | Balancia | Balancia |
Mechanical properties (annealed at room temperature)
Product shape | Thickness to diameter 4) d mm maximum | Yield resistance rp0.2 | Tensile strength | Elongation min. in% | |
N / mm2 | N / mm2 | Rm N / mm2 | A80mm1) ˂3mm thickness (longitudinal and transverse) | ||
C | 8 | 260 | 280 | 450 - 600 | 20 |
H | 13.5 | 240 | 260 | 450 - 600 | 18 |
P | 252) | 240 | 260 | 430 - 630 | 20 |
L3) | 100 | 240 | - | 400 - 630 | 20 (longitudinal) |
0.2% minimum yield strength value of high temperature ferritic steel
Product | Heat treatment conditions | 0.2% -Resistance to performance at temperature ° C | ||||||
100 | 150 | 200 | 250 | 300 | 350 | 400 | ||
C, H, P, L | Annealing | 220 | 215 | 210 | 205 | 200 | 195 | 190 |
Reference data for some physical properties
Density 20 ° C kg / m3 | 7,700 | |
Elastic modulus kN / mm2 at | 20°C | 220 |
200°C | 210 | |
400°C | 195 | |
500°C | - | |
Thermal conductivity W / m K 20 ° C | 25 | |
Specific heat capacity 20 ° CJ / kg K | 460 | |
Electrical resistivity 20 ° C Ω mm2 / m | 0.60 |
Average coefficient of linear thermal expansion 10 - 6 K - 1, between 20 ° C and
100°C10.5
200°C11.0
300°C11.5
400°C12.0
500°C12.0
Treatment
Above room temperature, low deformation cold forming is feasible. Sharp chamfering parallel to the rolling direction should be avoided. Plates with greater thickness and / or greater deformation will be preheated to 200 - 400 ° C. If applicable, Thermoforming may be required at 700 - 900 ° C. Corrosion resistance to the effects of annealed color or rust scale after forming or hot welding. Must be removed by pickling (pickling solution), grinding or sandblasting.Only non-ferrous tools are allowed for these jobs.Machining is no different from machining unalloyed carbon steel with equivalent or equivalent strength.